Interaction Between Interstitial Dislocation Loop and Micro-Crack in bcc Iron Investigated by Molecular Dynamics Method
JJ Liang and N Gao and YH Li, ACTA METALLURGICA SINICA, 56, 1286-1294 (2020).
In fission or fusion nuclear reactors, the interaction between the high energy particles (e.g. neutrons) and atoms would result in the radiation damages in materials, affecting the performance of materials and lifetime of reactors. The radiation hardening, embrittlement, swelling, creep, fatigue and so on are all related with the radiation damages in materials. Therefore, it is necessary to understand the underlying physics for developing the radiation resistant materials in future. Until now, the displacement cascade process has been studied for decades through computer simulation method. The other properties listed above have also been focused by different groups. However, in addition to these properties, it is also important to understand the degradation of mechanical properties induced by the supersaturated point defects and their clusters, especially the contribution from the interaction between dislocations and radiation defects. Under irradiation, in addition to the self-interstitial dislocation loops formed by the clustering of the self-interstitial atoms, the micro-crack can also be formed in bulk and near the surface of the materials, related with the gas bubble, grain boundary and blister, which would seriously influence the application of materials used in nuclear power plants. Under irradiation, in addition to the normal crack expansion under the effect of stress, these cracks would be key factors to irradiation assistant stress corrosion crack (IASCC) phenomena, which have been studied for decades. In previous studies, although the properties of self-interstitial dislocation loops and micro-crack have been studied independently, the interaction between them under the condition of irradiation has not been fully studied. In this work, the detailed interactions between self-interstitial dislocation loop and micro-crack in bcc iron have been studied at atomic scale with molecular dynamics (MD) simulation method. The results indicate that the relative position between them, the slope of micro- crack, the size of loop and existence of free surface, would all affect the interaction between loop and micro-crack and the related finally micro-structure after the interaction. Under different conditions, the interactions either induce the formation of micro-scale complex radiation damage structure, or the absorption of dislocation by micro- crack, resulting in the rugged crack tips, which would affect the growth and expansion of micro-crack, the degradation of mechanical properties of materials under irradiation. Furthermore, the results can also compare with the formation of dislocation and dislocation loop free zone near the crack tip observed experimentally, providing new understanding to these phenomena. Therefore, all these results provide new possible understandings of radiation damages.
Return to Publications page